Forging Square Stainless Steel 3mm 17 4ph Hot Rolled Forged Steel Shaft
1. Introduction
The deformation resistance of stainless steel at high temperature is relatively large, therefore, forging stainless steel needs to use a larger tonnage of equipment and wear resistant mold materials. The high temperature resistance of stainless steel is between nickel-based superalloy and general alloy structural steel, and the surface rises with the increase of the deformation degree, so too much deformation degree can not be used.
2. Chemical composition and mechanical Properties
| Chemical composition | |||||||||
| specifications | C | Mn | Si | Cr | Ni | P | S | Cu | Nb+Ta |
| 17-4PH(SUS630)UNS number S17400 | ≤0.07 | ≤1.00 | ≤1.00 | 15.5~17.5 | 3.0~5.0 | ≤0.04 | ≤0.03 | 3.0~5.0 | 0.15~0.45 |
3. Mechanical properties
Tensile strength σB (MPa) : 480℃ aging,≥1310; 550 ℃ ageing, p 1060; 580 ℃ ageing, p 1000; 620 ℃ ageing, p. 930
Conditional yield strength σ0.2 (MPa) : 480℃ aging,≥1180; 550 ℃ ageing, p 1000; 580 ℃ ageing, p 865; 620 ℃ ageing, p. 725
Elongation δ5 (%) : aging at 480℃,≥10; 550 ℃ ageing, 12 or higher; 580 ℃ ageing, 13 or higher; 620 ℃ ageing, 16 or higher
Section shrinkage ψ (%) : 480℃ aging,≥40; 550 ℃ ageing, 45 or higher; 580 ℃ ageing, 45 or higher; 620 ℃ ageing, 50 or more
Hardness: solid solution,≤363HB and ≤38HRC; Aging at 480℃,≥375HB and ≥40HRC; Aged at 550℃,≥331HB and ≥35HRC; Aging at 580℃,≥302HB and ≥31HRC; Aged at 620℃,≥277HB and ≥28HRC